| Título: | Análise experimental do efeito de fadiga em vergalhões de 8mm em barras isoladas e telas soldadas para aplicação em concreto armado |
| Autor: | Ferreira, Carol Chaves Mesquita e |
| Orientador(a): | Santos, Hudson Chagas dos |
| metadata.dc.contributor.referee1: | Santos, Hudson Chagas dos |
| metadata.dc.contributor.referee2: | Reis Sobrinho, José Francisco dos |
| metadata.dc.contributor.referee3: | Carvalho, Roberto Chust |
| metadata.dc.contributor.referee4: | Moreira, Maria de Lourdes Teixeira |
| Resumo: | O presente trabalho apresenta um estudo comparativo do comportamento de vergalhões CA-60 utilizados em estruturas de concreto armado na construção civil. Os aços que são incorporados ao concreto, na Engenharia Estrutural, podem se apresentar de duas formas, durante sua montagem: em barras isoladas, fixados por meio de arame recozido; e em formato de tela, com seus encontros soldados para a sua consolidação. Determinados sistemas estruturais, como pontes e edifícios-garagem, são constantemente submetidos às ações de fadiga devido a presença de cargas móveis, e que podem levar seus elementos a romperem com solicitações bem abaixo do limite de resistência às ações estáticas, que geralmente norteiam o dimensionamento das estruturas ao Estado Limite Último (ELU) do material. Assim, é primordial a verificação da resistência do aço, utilizado em estruturas com essas características, para a garantia da segurança do usuário durante a vida útil destas obras. Esta pesquisa foi realizada com a análise experimental de corpos de prova de vergalhões CA-60, de forma isolada e com ligações soldadas, com a realização de ensaios de fadiga em barras não envolvidas por concreto de diâmetro 8 mm. Foi gerada a Curva de Wöhler com os resultados dos ensaios de 36 corpos de prova, após a realização de vários testes para adoção das variações adotadas, comparando-se o comportamento dos vergalhões de aço CA-60 com a variação do número de ciclos, gerando ao fim a análise de três níveis de flutuação de tensão, para cada um das duas formas de execução das barras. Estudos com este tipo de aço em relação a esta resistência às flutuações ainda são escassos. Destaca-se que o aço CA-60 é produzido por meio de tratamento a frio, com a compactação do grão de forma mecânica, resultando em uma maior resistência às solicitações e dureza, e uma menor resistência à agressividade do meio (que pode produzir o efeito de corrosão) e a ductilidade. Sendo assim, este trabalho irá contribuir para um aprimoramento das considerações normativas para o dimensionamento ao ELU de estruturas de concreto armado em aços CA-60. |
| Abstract: | This research presents a comparative study of the behavior of CA-60 rebar used in reinforced concrete structures in civil construction. The steels that are incorporated in concrete in Structural Engineering can be presented in two formats, during their execution: in isolated rebars, fixed by means of wire with heat treatment; and in steel mesh, with their meetings welded for its consolidation. Certain structural systems, such as bridges and garage buildings, are constantly subjected to the fatigue actions generated by high loads, which can cause their elements to break with requests well below the limit of resistance to static actions, which are generally calculated to the last limit state of the material. Thus, it is essential to verify the strength of the steel, used in structures with these characteristics, to guarantee the safety of the user during the useful life of these constructions. This research was carried out with the experimental analysis of test specimens of CA-60 rebars, in an isolated form and with welded connections, with the realization of fatigue tests with bars in the air in rebars of diameter 8 mm. The Wöhler Curve was generated with the results of the tests of 36 test specimens, after several tests to the choice of the adopted variations, comparing the behavior of the steel bars CA-60 with the variation of the number of cycles, generating to the end the analysis of three levels of resistance fluctuations, for each one of two forms of execution of the bars. Studies with this type of steel in relation to this resistance to fluctuations are still scarce. It should be noted that CA-60 steel is produced by cold treatment, with mechanical compaction of the grain, resulting in a higher resistance to stress and hardness, and a lower resistance to aggression of the medium (which can generate corrosion ) and ductility. Thus, this work will contribute to an improvement of the normative considerations for the last limit state design of reinforced concrete structures in CA- 60 steels. |
| Palavras-chave: | Fadiga CA-60 Vergalhões Barras soldadas |
| Cnpq: | CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
| metadata.dc.language: | por |
| País: | Brasil |
| Editor: | Instituto Federal de Educação, Ciência e Tecnologia do Piauí |
| Sigla: | IFPI |
| Unidade: | Campus Teresina Central |
| metadata.dc.publisher.program: | PPGM |
| Citação: | FERREIRA, Carol Chaves Mesquita e. Análise experimental do efeito de fadiga em vergalhões de 8mm em barras isoladas e telas soldadas para aplicação em concreto armado. 2017. 119 f. Dissertação (Mestrado em Engenharia de Materiais) - Instituto Federal de Educação, Ciências e Tecnologia do Piauí, Teresina, 2017. |
| Tipo de acesso: | Acesso Aberto |
| URI: | https://bia.ifpi.edu.br/jspui/handle/123456789/760 |
| Data do documento: | 2017 |
| Aparece nas coleções: | Mestrado em Engenharia dos Materiais - Teresina Central |
Arquivos associados a este item:
| Arquivo | Descrição | Tamanho | Formato |
|---|
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.