Use este identificador para citar ou linkar para este item:
https://bia.ifpi.edu.br/jspui/handle/123456789/795| Tipo: | Dissertação |
| Título: | Influência do pó de cromo com adição de grafite sobre as propriedades mecânicas e morfológicas do revestimento duro produzido por soldagem MIG/MAG - CMT pulsante |
| Autor: | Borges, Guilherme Alceu Costa |
| Orientador(a): | Reis Sobrinho, José Francisco dos |
| Resumo: | O presente trabalho tem como objetivo avaliar as propriedades mecânicas e microes-truturais de revestimentos duros originados pelo processo de soldagem MIG/MAG CMT pulsante em um metal de base ASTM A36. Os corpos de prova foram preparados seguindo a recomendação de ensaio de revestimento conforme a norma ASME seção IX. Antes do processo de soldagem, aplicou-se sobre a superfície do metal de base de algumas amostras um pó a base de cromo e grafite com o intuito de facilitar a formação de carbetos de cromo e nas demais amostras não foi aplicado o pó de cromo. Para cada situação (com e sem o pó de cromo) aplicou-se três velocidades de soldagem, totalizando seis ensaios. O processo de soldagem MIG/MAG CMT pulsante foi completamente robotizado, utilizando-se o robô de soldagem KUKA, máquina de solda FRONIUS e como consumível o eletrodo AWS ER70S-6 de diâmetro 0,8 mm. Após a soldagem, realizou-se uma técnica conhecida como macrografia para deter-minar o percentual de diluição do cordão de solda. Avaliou-se as propriedades mecâ-nicas do metal de solda e do metal de base através de ensaios de dureza e microdu-reza. Para as análises microestruturais realizou-se a microscopia óptica (MO) e deter-minou-se a fases presentes nas amostras através do ensaio de DRX. Conseguiu-se realizar os objetivos propostos pelo trabalho e como resultados foi possível verificar que a aplicação do metal de solda (com ou sem o pó de cromo) contribuiu para au-mentar a dureza e a microdureza quando comparado com metal de base sem solda-gem; os melhores resultados de macrografia ocorreram nas velocidades de soldagem mais baixas, enquanto que os melhores resultados de propriedades mecânicas ocor-reram nos ensaios com maior velocidade de soldagem e que tiveram a aplicação do pó a base de cromo e grafite; verificou-se, também, a formação de carbetos de cromo na forma Cr7C3 na superfície do metal de solda o que contribui para a melhorias das propriedades mecânicas do revestimento duro. |
| Abstract: | The present work aims to evaluate the mechanical and microstructural properties of hard coatings originated by the pulsating MIG / MAG CMT welding process in an ASTM A36 base metal. The test specimens were prepared following the recommendation of the ASME standard IX section coating test. Before the welding process, a powder ba-sed on chromium and graphite was applied to the surface of the base metal of some samples in order to facilitate the formation of chromium carbides and in the other sam-ples the chromium powder was not applied. For each situation (with and without the chrome powder) three welding speeds were applied, totaling six tests. The pulsating MIG / MAG CMT welding process was completely robotized, using the KUKA welding robot, FRO-NIUS welding machine and as consumable the AWS ER70S-6 electrode with a diameter of 0.8 mm. After welding, a technique known as macrography was performed to determine the percentage of dilution of the weld bead. The mechanical properties of the weld metal and the base metal were evaluated by hardness and mi-crohardness tests. Microstructural analysis was performed by optical microscopy (OM) and the phases present in the samples were determined by the XRD assay. It was possible to realize the objectives proposed by the work and as results it was possible to verify that the application of the weld metal (with or without the chromium powder) contributed to increase the hardness and the microhardness when compared with base metal without welding; the best machining results occurred at the lowest welding spe-eds, while the best results of mechanical properties occurred in the tests with the highest welding speed and with the application of the powder based on chromium and graphite; the formation of chromium carbides in the Cr7C3 form on the surface of the weld metal has also been verified which contributes to improvements in the mechanical properties of the hard coating. |
| Palavras-chave: | Soldagem Propriedades mecânicas Revestimento duro |
| Cnpq: | CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
| metadata.dc.language: | por |
| País: | Brasil |
| Editor: | Instituto Federal de Educação, Ciência e Tecnologia do Piauí |
| Sigla: | IFPI |
| Unidade: | Campus Teresina Central |
| metadata.dc.publisher.program: | PPGM |
| Citação: | BORGES, Guilherme Alceu Costa. Influência do pó de cromo com adição de grafite sobre as propriedades mecânicas e morfológicas do revestimento duro produzido por soldagem MIG/MAG - CMT pulsante. 2019. Dissertação (Mestrado em Engenharia de Materiais) - Instituto Federal de Educação, Ciência e Tecnologia do Piauí, Teresina, 2019. |
| Tipo de acesso: | Acesso Aberto |
| URI: | https://bia.ifpi.edu.br/jspui/handle/123456789/795 |
| Data do documento: | 2019 |
| Aparece nas coleções: | Mestrado em Engenharia dos Materiais - Teresina Central |
Arquivos associados a este item:
| Arquivo | Descrição | Tamanho | Formato |
|---|
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.